2 化学成分
化 学 成 分,% | |||||
C | Si | Mn | P | S | Ceq |
≤0.18 | ≤0.55 | ≤1.98 | ≤0.025 | ≤0.020 | ≤0.50 |
2) 碳当量(Ceq,%)计算公式如: Ceq(%)=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15
3 常用规格尺寸
材质- | 厚度mm | 宽度mm | 长度mm |
WH60A | 8-12 | 2000-2500 | 8000-12000 |
WH60A | 12-16 | 2000-2500 | 8000-12000 |
WH60A | 16-50 | 2000-2500 | 8000-12000 |
WH60A | 50-80 | 2000-2500 | 8000-12000 |
WH60A | 80-100 | 2000-2500 | 8000-12000 |
WH60A | 100-120 | 2000-2500 | 8000-12000 |
WH60A | 120-150 | 2000-2500 | 8000-12000 |
WH60A | 150-200 | 2000-2500 | 8000-12000 |
材质 | 厚度 | 宽度 | 长度 |
WH60A | 8 | 2200 | 12000 |
WH60A | 10 | 2200 | 10000 |
WH60A | 10 | 2480 | 10000 |
WH60A | 12 | 2500 | 12000 |
WH60A | 16 | 2500 | 13000 |
WH60A | 20 | 2500 | 12800 |
WH60A | 25 | 2350 | 12000 |
WH60A | 30 | 2200 | 12000 |
WH60A | 35 | 2200 | 10000 |
WH60A | 40 | 2500 | 11000 |
WH60A | 45 | 3040 | 12950 |
WH60A | 50 | 2450 | 11100 |
WH60A | 60 | 2200 | 11800 |
WH60A | 70 | 2200 | 12000 |
WH60A | 80 | 2200 | 12000 |
WH60A | 90 | 2200 | 10000 |
WH60A | 100 | 2200 | 10000 |
WH60A | 120 | 2300 | 12300 |
WH60A | 150 | 2300 | 10500 |
WH60A | 150 | 2300 | 8350 |
4 力学性能
牌号 | 规格 | 拉伸性能 | AKv,J,纵向 | 延伸率 | 180°弯曲试验 d=弯心直径 a=试样厚度 |
WH60A | ≤16 | ≥460 | 560- 780 | ≥ 17 | d=2a |
>16-35 | ≥440 | d=3a | |||
>35-50 | ≥420 | ||||
>50-100 | ≥400 |
7 各项检验的检验项目、取样数量、取样方法和实验方法
序号 | 检验项目 | 取样数量(个) | 取样方法 | 试验方法 |
1 | 化学分析 | 1(每炉罐号) | GB/T222 | GB/T223 |
2 | 拉伸 | 1 | GB/T2975 | GB/T228 |
3 | 夏比冲击 (V型缺口) | 3 | GB/T2975 | GB/T229 |
4 | 弯曲 | 1 | GB/T2975 | GB/T232 |